- Process of Reversion and Mechanical Properties in Metastable Austenitic Stainless Steels Containing Molybdenum
- Mo オ フクム ジュン アンテイ オーステナイトケイ ステンレス コウ ノ
この論文をさがす
抄録
Effect of molybdenum on the behavior of reversion of deformation induced martensite to austenite and the mechanical properties of specimens containing reversed austenite were investigated within (15.5 13)% Cr-11%Ni-(02.5)%Mo steels by means of transmission electron microscopy, magnetic analysis and tensile testing. Reversion treatment of martensite to austenite was performed at a higher heating rate using a salt bath and at lower heating rate using an electric furnace. The results obtained are as follows.<BR>(1) The steels used almost transform to lath martensite ( a') from austenite (γ) by 90% cold rolling at 290 K. Effect of molybdenum on y stability against deformation is almost same as that of chromium.<BR>(2) The temperature range for reversion rises with increasing molybdenum content.<BR>(3) In case of 923 K annealing at a higher heating rate, a process of reversion is changed from a martensitic type to a diffusional one with increasing molybdenum content. A 13%Cr-11%Ni-2.5%Mo steel which reverts to γ by a diffusional process has an ultra fine austenitic structure with a mean grain size of 0.2 μm giving a high 0.2% proof stress of 0.8 GPa, tensile strength of 1.0 GPa, and elongation of 30%.<BR>(4) In case of 923 K annealing at a lower heating rate, a' reverts to γ by a diffusional process at lower heating temperatures. Therefore, molybdnum content of 0.5% is enough to obtain a high strergth steel.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 76 (10), 1728-1735, 1990
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680161210112
-
- NII論文ID
- 110001492487
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3694367
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可