BaO-BaF<SUB>2</SUB>系融体への炭酸ガスの溶解度

• 原 茂太

  大阪大学工学部 工博

• 石田 哲夫

  大阪大学大学院(現:松下電子工業(株))

• 菅野 浩至

  大阪大学大学院(現:新日本製鉄(株))

• 荻野 和己

  大阪大学工学部 工博(現:香川職業訓練短期大学校))

書誌事項

タイトル別名

• Solubility of Carbon Dioxide in BaO-BaF<SUB>2</SUB> Melts
• BaO-BaF2系融体への炭酸ガスの溶解度
• BaO BaF2ケイ ユウタイ エ ノ タンサン ガス ノ ヨウカイド

抄録

Equilibrium CO₂ partial pressures in the systems BaO-BaCO₃ and BaO-BaCO₃-BaF₂ were measured by using the thermo-balance. The results are summarized as follows, <BR>(1) Dissociation of BaCO₃ under P_CO<SUB>2</SUB> = 1 atm occurs at 1645 K and the temperature decreases with decreasing the partial pressure of CO₂.<BR>(2) Interaction parameter on the assumption of regular solution for BaO-BaCO₃ melts changed from -23 kJ/mol at 1598 K to -15 kJ/mol at 1773 K.<BR>(3) Gibbs energy of the reaction BaO (melt) + CO₂(g) = BaCO₃(melt)ΔG°is given by the following relation, <BR>ΔG°=-0.152T + 279(kJ/mol)<BR>(4) Assuming that BaO-BaCO₃-BaF₂ melts behave as the regular solution, the calculated values of solubility of CO₂ in BaO-BaF₂ melts are fairly in good agreement with measured ones except for those under P_CO<SUB>2</SUB> = 1 atm.

収録刊行物

• 鉄と鋼

  鉄と鋼 78 (11), 1666-1673, 1992

  一般社団法人 日本鉄鋼協会

キーワード

• BaO-BaCO<SUB>3</SUB>
• BaO-BaCO<SUB>3</SUB>-BaF<SUB>2</SUB>
• melt
• solubility of CO<SUB>2</SUB>
• Gibbs energy
• regular solution

詳細情報

• CRID: 1390001205152523392
• NII論文ID: 110001493108
• NII書誌ID: AN00151251
• DOI: 10.2355/tetsutohagane1955.78.11_1666
• ISSN: 18832954
• ISSN: 00211575
• NDL書誌ID: 3798306
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3798306
• Web Site: https://www.jstage.jst.go.jp/article/tetsutohagane1955/78/11/78_11_1666/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可