炭材内装熱間成型ブリケットの強度発現機構

• 笠井 昭人

  (株)神戸製鋼所加古川製鉄所

• 松井 良行

  (株)神戸製鋼所加古川製鉄所

• 野間 文雄

  (株)神戸製鋼所加古川製鉄所

• 岩切 治久

  (株)神戸製鋼所加古川製鉄所

• 清水 正賢

  (株)神戸製鋼所加古川製鉄所(現:九州大学大学院工学研究院)

書誌事項

タイトル別名

• Cold Strength Enhancement Mechanism of Carbon Composite Iron Ore Hot Briquet
• タンザイ ナイソウ ネツカン セイケイ ブリケット ノ キョウド ハツゲン キコウ

抄録

Hot briquetting process was proposed as a new manufacturing method of carbon composite iron are briquet. The process was a binder-less briquetting in use of thermal plasticity of coal. The briquet by hot briquetting was higher apparent density and lower porosity than a cold bonded briquet.<BR>In order to enhance a cold strength and an apparent density of the briquet, the briquet was made by a double roll type briquetting machine at various conditions. Effects of hot briquetting conditions and coal properties on the briquet properties were investigated and the cold strength was discussed relating to pore structure of the briquet.<BR>Porosity and crushing strength of the briquet changed with hot briquetting temperature. Crushing strength of the briquet had a maximum value at near temperature standing at maximum fluidity of coal measured by Gieseler plastometer. Increasing maximum fluidity as caking property of coal, crushing strength of the briquet increased with decreasing in the briquet porosity and increasing in coherence to coal and iron ore.

収録刊行物

• 鉄と鋼

  鉄と鋼 87 (5), 313-319, 2001

  一般社団法人 日本鉄鋼協会

キーワード

• hot briquetting
• carbon composite iron ore briquet
• crushing strength
• porosity
• maximum fluidity

詳細情報

• CRID: 1390282680159816832
• NII論文ID: 110001844651
• NII書誌ID: AN00151251
• DOI: 10.2355/tetsutohagane1955.87.5_313
• ISSN: 18832954
• ISSN: 00211575
• ISSN: http://id.crossref.org/issn/00211575
• NDL書誌ID: 5754028
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I5754028
• Web Site: https://www.jstage.jst.go.jp/article/tetsutohagane1955/87/5/87_5_313/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可