- 西村 富隆
- 日本特殊鋼株式会社
書誌事項
- タイトル別名
-
- On the High-Chromium High-Cobalt Type Steels for Hot Work Dies
- コウクロム コウコバルトケイ ネツカン ダイス コウ ニ ツイテ
- 高クロム高コバルト系熱間ダイス鋼にについて
- コウクロム コウコバルトケイ ネツカン ダイス コウ ニ ニ ツイテ
この論文をさがす
抄録
The fundamental characteristics of 12Cr-7W-0.5V-5Co (DSE) and 12Cr-7W-0.5V-10Co (DSF) type steels for hot work dies have been investigated.The results obtained are as follows:<BR>(1) Transformation temperature on heating, specific gravity, specific heat and coefficient of thermal expansion are measured, and particularly it is noticeable that the coefficients of thermal expansion show small values.<BR>(2) Secondary hardening occurs in the temperature range from 500 to 550°C, and that resistance to tempering softening becomes larger with increasing austenitizing temperature. The temperature range suitable for hardening is from 1050 to 1100°C, so the austenitizing temperature of 1050°C only is used for all tests.<BR>(3) The nose of isothermal transformation curve situates at the temperature of 750°C and 15min for DSE, and 750°C and 25min for DSF.Ms temperature is 205°C for DSE and 175°C for DSF.<BR>(4) At the testing temperature of 600°C, hardness, tensile strength and impact strength are Hv 225, 93 kg/mm2 and 8 kg m/cm2 for DSE, and Hv 270, 107 kg /mm2 and 5 kg m/cm2 for DSF.<BR>(5) The dimensional change of a round bar at the tempering temperature of 600°C is +0.045% for DSE and + 0.040% for DSF in the direction of diameter, and 0% for DSE and -0.010% for DSF in the direction of length.<BR>(6) The tempering at 600°C gives the best impact strength and wear resistance at room temperature.<BR>(7) When both steels are isothermally tempered for 1000 hr at 600, 650 and 700°C, hardness decreases linearly and impact strength slightly with increasing tempering time at each temperature.<BR>And in the process of these temperings, the following sequence of changes in carbides takes place: M6C+M7C3→M6C+M7C3+M23C6→M6C+M23C6→6C+M23C6+Fe2W→M23C6+Fe2W.<BR>(8) Resistance to heat checking is better than that of SKD5 (JIS) steel of 10W-3Cr-0.5V type.<BR>(9) Resistance to oxidation at high temperatures is very excellent as compared with SKD 5 steel.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 50 (10), 1449-1457, 1964
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680104121472
-
- NII論文ID
- 130005615340
- 110001869868
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可