- Effect of Oxide Inclusions on MnS Precipitation in Low Carbon Steel
- テイ タンソ コウチュウ ノ MnS ノ セキシュツ ニ オヨボス サンカブツ
この論文をさがす
抄録
It has been known that precipitates of MnS become effective nuclei of intragranular ferrite during A3 transformation and improve the ductility of steels. The objective of this work is to investigate the effect of oxide inclusions on MnS precipitation after solidification in order to obtain uniform distribution of precipitates. Various deoxidizing elements were added to low carbon steel melt of 1 kg. This steel melt was solidified in an alumina crucible after some killing time. The nonmetallic inclusions were analysed by two-dimensional X-ray microanalyser on a cross-section of the ingot specimen. Among deoxidizing elements, the number of oxide inclusions of Hf, Ce, Y or Zr was greater and the distribution was more uniform than that of Al or Ti. The precipitation of MnS was followed effectively on those oxide inclusions between 1 100 and 1 400°C. The kinetics of precipitation was analysed by a precipitation model taking into account solidification and δ/γ transformation. The low diffusivity of Mn causes the depletion of Mn around MnS precipitates. It was considered that this Mn depletion promoted ferrite nucleation.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 75 (3), 501-508, 1989
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680160831104
-
- NII論文ID
- 110001870627
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 3222632
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可