Temperature Dependence of Complex Dielectric Constant of TGS Powders
-
- Emoto Tomomasa
- Faculty of Science, Hiroshima University
-
- Motegi Hiroshi
- Faculty of Science, Hiroshima University
-
- Nakamura Eiji
- Faculty of Science, Hiroshima University
書誌事項
- タイトル別名
-
- Temperature Dependence of Complex Diele
この論文をさがす
抄録
The real part ε′ and the imaginary part ε″ of the complex dielectric constant of TGS powders have been measured precisely at 1 kHz as functions of temperature from 40°C to 58°C. Powders separated into different particle sizes using sieves ranging from 25 μm to 210 μm in mesh size were used as specimens. A well defined peak of ε′ at 49°C (Tc), indicating ferroelectric phase transition, was observed on the specimen with particle size less than 25 μm, as well as on the specimens with larger particle sizes. The thickness of the nonferroelectric surface layer should be far smaller than 20 μm, the thickness reported by Mansingh and Bawa. Both components of the complex dielectric constant showed remarkable particle size dependence. Behaviors of ε′ and ε″ below Tc are explained by considering the domain wall motion, and the origin of ε″ above Tc is attributed to the ionic conduction.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 46 (3), 876-880, 1979
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204189792384
-
- NII論文ID
- 110001964332
- 130003737705
- 210000088016
-
- NII書誌ID
- AA00704814
-
- BIBCODE
- 1979JPSJ...46..876E
-
- COI
- 1:CAS:528:DyaE1MXhs1Sqsbs%3D
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 2043605
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可