- Layer Structures of Cu<I><SUB>x</SUB></I>Ag<SUB>1−<I>x</I></SUB>I Crystals
- Layer Structures of Cu<sub><i>x</i></sub>Ag<sub>1-<i>x</i></sub>I Crystals
この論文をさがす
抄録
X-ray diffraction studies were made on layer structures in the quasi-binary system CuI–AgI and their structural changes were investigated by standing them at room temperature and by heating. The proportion of Cu to Ag in a crystal was determined by the atomic absorption method. The following facts were revealed. The CuxAg1−xI crystals have faulted 2H structures, which often coexist with long-period polytypes, in the composition range 0<x<0.025, the 4H structure in 0.025≤x≤0.034, the 4H structure immediately after growth in 0.061≤x≤0.092 and the 3R structure (the zincblende-type structure) in 0.148≤x≤0.277. The 4H structure in the range 0.061≤x≤0.092 changes to twins of the 3R at room temperature and this structural change occurs earlier with increasing x value. The 3R structure is stable at high temperatures below 146°C over the range x≥0.025. Reduced lattice parameters of the layer structures decrease with the increase of Cu concentration and the Cu ion is substituted for the Ag ion.
収録刊行物
-
- Journal of the Physical Society of Japan
-
Journal of the Physical Society of Japan 49 (1), 285-289, 1980
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204184693248
-
- NII論文ID
- 210000088999
- 110001965085
-
- NII書誌ID
- AA00704814
-
- BIBCODE
- 1980JPSJ...49..285M
-
- COI
- 1:CAS:528:DyaL3cXltVGjs70%3D
-
- ISSN
- 13474073
- 00319015
-
- NDL書誌ID
- 2185291
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可