BaTiO<sub>3</sub>の焼結と微細構造に及ぼすLi<sub>2</sub>Si<sub>2</sub>O<sub>5</sub>の影響
-
- PURWASASMITA Bambang Sunendar
- Department of Materials Science, Faculty of Science and Technology
-
- 星 英梨子
- 慶應義塾大学大学院理工学研究科
-
- 木村 敏夫
- 慶應義塾大学大学院理工学研究科
書誌事項
- タイトル別名
-
- Effect of Li2Si2O5 Addition on the Sintering and Microstructure of BaTiO3.
この論文をさがす
抄録
Densification behavior and micro structural characteristics were examined for BaTiO3 containing 0.25-2.00mass% Li2Si2O5. Li2Si2O5 lowered the sintering temperature of BaTiO3. The optimum concentration to obtain high density was 1mass%. A concentration smaller than the optimum value did not effectively lower the sintering temperature, while a larger concentration resulted in the formation of inhomogeneous microstructure. There was an optimum sintering temperature to obtain compacts with maximum density. Extensive grain growth occurred above the optimum temperature. The grain boundary phase, which was a liquid phase at the sintering temperature, contained TiO2-rich particles, whose distribution was non-uniform. The formation mechanisms of such microstructure were discussed.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 109 (1267), 191-196, 2001
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680225879552
-
- NII論文ID
- 110002288746
-
- NII書誌ID
- AN10040326
-
- COI
- 1:CAS:528:DC%2BD3MXisV2hsL0%3D
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 5690864
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可