- Change in Solution pH inside Microcracks in Glass and Its Effect on Subcritical Crack Growth.
- ガラス ニ オケル ビショウ クラック ナイ ノ pH ヘンカ ト ソノ クラック セイチョウ エ ノ エイキョウ
この論文をさがす
抄録
The effect of changing the solution pH inside indentation-induced microcracks on the post-indentation crack-growth behavior was investigated in glass. Buffer solution was used for crack growth experiments in order to suppress the pH change inside the microcracks and then comparison of crack growth behavior was made between the buffered and unbuffered solutions. It was found that the pH change inside the microcracks occurs depending on the initial pH of the solution and that the bonding state at the crack tip region changes depending on the pH change inside the microcracks. The obtained results also showed that the ratio of surface area/solution volume, S/V affects the pH change inside microcracks, which induced the change in the stress corrosion limit, Kscc depending on the pH.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 107 (1250), 983-985, 1999
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680224942976
-
- NII論文ID
- 110002289822
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 4867477
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可