- Fabrication and Some Mechanical Properties of SiC Whisker-Reinforced Si<sub>3</sub>N<sub>4</sub> Composites Utilizing Underwater-Shock Pressure
- スイチュウ ショウゲキ アツリョク ニ ヨル SiC ウイスカー キョウカ チ
この論文をさがす
抄録
SiC whisker-reinforced Si3N4-based composites without additives were compacted by underwater-shock wave. The composites contained 10, 20 and 30vol% SiC whisker as reinforcements. There were no macrocracks in all shock compacted composites. The as-compacted and specimens sintered at various temperatures for 5h were characterized by the measurements of relative density, micro Vickers hardness and fracture toughness. The relative density of a sintered Si3N4-10vol% SiC whisker composite was higher than that of sintered Si3N4-20 and 30vol% SiC whisker composites, and reached the theoretical density by sintering at 1973K. Hardness of each composite increased up to 1823K in proportion to sintering temperature, and then saturated above 1823K. The hardness and fracture toughness of the Si3N4-30vol% SiC whisker composite sintered at 1973K were about 29GPa and 5.0MPa√m, respectively. The fracture toughness was 25% higher than those of monolithic Si3N4 and other obtained composites sintered at the same temperature. SEM observation showed that whisker bridging and deflection were observed in sintered composites and that the matrix of the Si3N4-30vol% SiC whisker composite consisted of plate-like and submicron order fine needle-like β-Si3N4 grains.
収録刊行物
-
- Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)
-
Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 101 (1172), 445-450, 1993
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205277154560
-
- NII論文ID
- 110002290335
-
- NII書誌ID
- AN10040326
-
- ISSN
- 18821022
- 09145400
-
- NDL書誌ID
- 3825500
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可