炭化ケイ素傾斜炭素材のムライト被覆とその耐酸化性

• 山本 修

  神奈川工科大学工業化学工学科

• 笹本 忠

  神奈川工科大学工業化学工学科

• 稲垣 道夫

  北海道大学工学部応用化学科

書誌事項

タイトル別名

• Coating of SiC-Gradient Carbon Material with Mullite Film and Its Oxidation Resistance
• タンカ ケイソ ケイシャ タンソザイ ノ ムライト ヒフク ト ソノ タイ サ

抄録

The optimum conditions for mullite coating on SiC-gradient carbon substrates and its oxidation resistance were studied. A homogeneous precursor solution with the composition of Al/Si=3 was prepared by refluxing an ethanol solution of Al(NO₃)₃ and silicon ethoxide (TEOS) of 0.1mol/l at its boiling point for 12h. A mullite film with a thickness of 1.0μm without any cracks was obtained under the following conditions; the drawing up the substrate from the precursor solution at a rate of 0.05cm/s, keeping at room temperature for 24h and at 100°C for 48h in air, and then heating up to 1300°C at a rate of 200°C/h. The SiC-gradient carbon substrates coated with the mullite film showed the excellent oxidation resistance; no appreciable weight loss by oxidation at 1000°C for 15h was observed.

収録刊行物

• Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)

  Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 102 (1182), 165-169, 1994

  公益社団法人 日本セラミックス協会

キーワード

• Mullite
• Gradient materials
• SiC
• Carbon
• Oxidation resistance
• Sol-gel process

詳細情報

• CRID: 1390282680255270400
• NII論文ID: 110002290531
• NII書誌ID: AN10040326
• DOI: 10.2109/jcersj.102.165
• COI: 1:CAS:528:DyaK2cXit1Ckurc%3D
• ISSN: 18821022
• ISSN: 09145400
• NDL書誌ID: 3865711
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3865711
• Web Site: http://www.jstage.jst.go.jp/article/jcersj1988/102/1182/102_1182_165/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可