超音波噴霧熱分解法による球状Pd金属粉末の合成に及ぼす出発原料の影響

DOI Web Site Web Site 被引用文献9件 参考文献13件

書誌事項

タイトル別名
  • Effects of Starting Materials on the Preparation of Spherical Pd Powders by Ultrasonic Spray Pyrolysis
  • チョウオンパ フンム ネツ ブンカイホウ ニヨル キュウジョウ Pd キンゾク

この論文をさがす

抄録

Palladium powders were prepared from aqueous solutions of Pd(NO3)2, PdCl2 and Pd(NH3)4Cl2 by ultrasonic spray pyrolysis in nitrogen flow and the effects of starting materials and preparation conditions on the properties of prepared powders were investigated. Submicron powders were obtained from PdCl2 because it melts at 680°C and disintegrates on evolving gas. Powders prepared from Pd(NH3)4Cl2 often had a bimodal particle size distribution and irregular shapes because the porous particles of Pd formed at about 300°C underwent either sintering or breaking up to pieces at higher temperatures, resulting in a mixture of large and small particles. Spherical solid powders were prepared from Pd(NH3)4Cl2 only when the synthesis condition was carefully controlled within a narrow range. Dense spherical powders were obtained in a wide range of preparation condition by using Pd(NO3)2. Pd(NO3)2 hydrolyzes in heated droplets and then dissociates to PdO. At higher temperatures Pd particles formed by the dissociation of PdO sinter and densify successively to form single-crystal-like solid particles. Pd powders prepared from Pd(NO3)2 and Pd(NH3)4Cl2 oxidize less when they are heated in air.

収録刊行物

被引用文献 (9)*注記

もっと見る

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ