前駆体ポリ (イソプロピルイミノアラン) から合成した窒化アルミニウムのキャラクタリゼーション

• 斉藤 康夫

  早稲田大学理工学部応用化学科

• 小山 誠一

  早稲田大学理工学部応用化学科

• 菅原 義之

  早稲田大学理工学部応用化学科

• 黒田 一幸

  早稲田大学理工学部応用化学科 早稲田大学各務記念材料技術研究所

書誌事項

タイトル別名

• Characterization of Aluminum Nitride from a Precursor Poly (isopropyliminoalane)
• Characterization of Aluminum Nitride fr

抄録

Aluminum nitride (AlN) was prepared by pyrolysis of poly (isopropyliminoalane) under Ar and NH₃/N₂ atmospheres. X-ray powder diffraction analysis revealed that the only crystalline phase was AlN, whose lattice constants showed that possible amounts of carbon and oxygen in the lattice should be very small. Chemical analyses showed the presence of carbon only in the product pyrolyzed in Ar; almost all carbon was removed by pyrolysis in NH₃/N₂. The ceramic yield for two-step pyrolysis in Ar (1000°C for 2h, 1600°C for 2h) was 32%, while that for pyrolysis in NH₃/N₂ (600°C for 2h in NH₃, 1350°C for 8h in N₂) was 47%.

収録刊行物

• Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)

  Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 104 (1206), 143-145, 1996

  公益社団法人 日本セラミックス協会

キーワード

• Aluminum nitride
• Precursor
• Poly (isopropyliminoalane)
• Pyrolysis

詳細情報

• CRID: 1390001205277079296
• NII論文ID: 110002291327
• NII書誌ID: AN10040326
• DOI: 10.2109/jcersj.104.143
• ISSN: 18821022
• ISSN: 09145400
• ISSN: http://id.crossref.org/issn/09145400
• NDL書誌ID: 3926680
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3926680
• Web Site: http://www.jstage.jst.go.jp/article/jcersj1988/104/1206/104_1206_143/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可