アンモニウムアルミニウム炭酸塩 (AACH) から生成するアルミナの相転移過程

• 林 浩一

  (株) 東陶機器基礎研究所

• 豊田 誠司

  九州大学大学院

• 武部 博倫

  九州大学大学院

• 森永 健次

  九州大学大学院総合理工学研究科材料開発工学専攻

書誌事項

タイトル別名

• Phase Transformations of Alumina Derived from Ammonium Aluminum Carbonate Hydroxide (AACH)
• アンモニウム アルミニウム タンサンエン AACH カラ セイセイスル アルミ

抄録

The thermal decomposition and the phase transformations of ammonium aluminum carbonate hydroxide (AACH) to α-alumina have been studied. Amorphous-, γ- and θ-alumina were identified as intermediate products. A TTT diagram for the process of the thermal decomposition and the phase transformations was determined. Kinetic analysis of the θ- to α-aluminas transformation by the Avrami-Erofeev equation showed that the transformation occurred by the nucleation and growth mechanism. Results of transmission electron microscopy (TEM), however, suggested that the transformation occurred by the synchro-shear mechanism. The maximum particle size of θ-alumina and the minimum particle size of α-alumina were approximately 30 and 40nm, respectively. A model of the transformation was presented from the viewpoint of crystallography.

収録刊行物

• Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌)

  Journal of the Ceramic Society of Japan (日本セラミックス協会学術論文誌) 99 (1151), 550-555, 1991

  公益社団法人 日本セラミックス協会

キーワード

• Transformation
• Ammonium aluminum carbonate hydroxide (AACH)
• α-alumina
• θ-alumina
• Kinetics
• Synchro-shear
• Crystallography

詳細情報

• CRID: 1390001205276528896
• NII論文ID: 110002292041
• NII書誌ID: AN10040326
• DOI: 10.2109/jcersj.99.550
• ISSN: 18821022
• ISSN: 09145400
• ISSN: http://id.crossref.org/issn/09145400
• NDL書誌ID: 3731746
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3731746
• Web Site: http://www.jstage.jst.go.jp/article/jcersj1988/99/1151/99_1151_550/_pdf
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可