- Polymer Materials. Sub-Relaxation of Bisphenol a Polycarbonate Studied with Dynamic Birefringence.
- ビスフェノール A ポリカーボネート ノ フクブンサン ドウテキフククッセツ ニ ヨル ケントウ
この論文をさがす
抄録
Dynamic birefringence and dynamic viscoelasticity of bisphenol A polycarbonate were simultaneously measured over a wide range of temperature from -150 to 180°C. Large γ dispersion observed for the complex Young's modulus was found to be inactive for the complex strain-optical coefficients, which is the ratio of birefringence to the strain. The present result indicates that γ dispersion cannot be attributed to the reorientation of any atomic groups, but to the relaxation of internal strain by translational motions. Dynamic birefringence was anticipated to be a new experimental method for the subrelaxation of glassy polymers.
収録刊行物
-
- 材料
-
材料 49 (12), 1298-1300, 2000
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205391410560
-
- NII論文ID
- 110002293925
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 5600314
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可