- Nanoscopic In-situ Visualization of Stress Corrosion Crack Growth by STM/AFM.
- STM AFM ニ ヨル オウリョク フショク ワレ キレツ シンテン ノ ソ
この論文をさがす
抄録
Most damage issues in machines and structures are caused by environmentally induced material degradation in an operating environment, including stress corrosion (SC) cracking. In order to clarify the fracture and damage mechanisms of these environmentally induced material degradation, serial high-magnification obsearvation of damage initiation and growth stages is necessary. In this investigation, the authors demonstrate that atomic force microscopy (AFM) is very much capable of performing in-situ nanoscopic visualization of growth processes of SC cracking in an aqueous solution and in a laboratory air. The nanoscopic growth mechanisms of SC crack growth of a high-strength aluminum alloy and an austenitic stainless steel are discussed based upon nanoscopic in-situ visualization by AFM and scanning tunneling microscope (STM).
収録刊行物
-
- 材料
-
材料 43 (486), 336-342, 1994
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680370061312
-
- NII論文ID
- 110002294130
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DyaK2cXkvVynt78%3D
-
- ISSN
- 18807488
- 05145163
- http://id.crossref.org/issn/05145163
-
- NDL書誌ID
- 3859299
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可