Occurrence of Supersaturated Solution with Respect to Ca(OH)<sub>2</sub> in Portland Cement Paste
-
- KONDO Wakichi
- National Chemical Laboratory for Industry
-
- FUJII Kinjiro
- National Chemical Laboratory for Industry
Bibliographic Information
- Other Title
-
- セメントの初期水和におけるCa(OH)<sub>2</sub>の過飽和溶解
- セメント ノ ショキ スイワ ニ オケル Ca OH 2 ノ カホウワ ヨウカイ
Search this article
Abstract
As a measure of supersaturation with respect to Ca(OH)2 in the solution of portland cement paste, W/C=0.6, a saturation ratio was used, which was defined by the ratio of actually determined product m′Ca2+⋅m′2OH- to the solubility product, both in molalities, at the same ionic strength. For three of five cements examined, there was seen the time correspondance between the occurrence of maximum saturation ratio of about 3 and the beginning of intensive rise of heat liberation rate. This was ture for the cement paste with or without addition of soluble salt after pre-leaching treatment of cement with a large amount of water. For the other two cements, the maximum saturation ratio was established in an hour, while the rise of heat liberation rate was two to three hours late.
Journal
-
- Journal of the Ceramic Association, Japan
-
Journal of the Ceramic Association, Japan 82 (946), 333-336, 1974
The Ceramic Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001205248744832
-
- NII Article ID
- 110002308198
-
- NII Book ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL BIB ID
- 7652346
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed