- Solid State Reaction between Y<sub>2</sub>O<sub>3</sub> and Nb<sub>2</sub>O<sub>5</sub>
- Y2O3 Nb2O5ケイ ノ コソウ ハンノウ
この論文をさがす
抄録
Solid state reactions between sintered Y2O3 and Nb2O5 have been studied from 1275°C to 1350°C, in which two kinds of sintered Y2O3, 70 and 95% dense, were employed. Techniques used were electron microscopy, EPMA, X-ray diffraction and dilatometry.<br>A layer of Y2O3⋅Nb2O5 formed at the Y2O3-Nb2O5 interface, of which growth was controlled by the one-way diffusion of Nb2O5 across the product layer. The apparent activation energies of the diffusion for 70% and 95% dense Y2O3 are 150 and 200kcal/mol, respectively.<br>EPMA of 1350°C-specimen showed the concentration gradient of Nb across the reaction layer ranging from 50 to 55mol% of Nb2O5 increasing towards the Y2O3⋅Nb2O5-Nb2O5 interface. The observed separation of diffusion couples is probably due to the difference of thermal expansion coefficients between the product and Nb2O5.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 86 (989), 7-11, 1978
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205248070016
-
- NII論文ID
- 110002309793
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- HANDLE
- 10191/7515
-
- NDL書誌ID
- 1926440
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可