- The Formation of α-FeOOH from Fe(OH)<sub>2</sub> Gel by the Dissolution-Precipitation Process
- スイサンカ テツ 2 ゲル ノ サンカ ニ オケル アルファ FeOOH ノ
この論文をさがす
抄録
Coarse crystals of Fe(OH)2 were prepared by adding iron (II) sulfate solutions to concentrated sodium hydroxide solutions at around 80°C. The Fe(OH)2 gel was oxidized at 7°C by air bubbling. The oxidation of Fe(OH)2 proceeded by the zeroorder reaction with its rate independent of the size of hexagonal Fe(OH)2 crystals which turned into acicular α-FeOOH crystals. The rate-determining step of the oxidation may be the dissolution of oxygen into the solution. In the oxidation process of the coarse Fe(OH)2 gels, star-shaped aggregates composed of six α-FeOOH crystals were formed Electron-diffraction analysis of the star-shaped aggregates indicated that the six equivalent [100] directions in the hexagonal crystal of Fe(OH)2 coincide with the [010] direction in each of six crystals of orthorhombic α-FeOOH. The oxygen arrangement on the (100)hex planes of Fe(OH)2 is equivalent to that on the (010)orth planes of α-FeOOH. It is concluded that Fe(OH)2 crystals in the solution are oxidized selectively on their (100) planes, followed by epitaxial growth of α-FeOOH.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 94 (1096), 1201-1205, 1986
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680225257216
-
- NII論文ID
- 110002313535
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3106643
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可