- Mechanical Properties and Existing Phases of Composite Ceramics Obtained by Sintering of a Mixture of Hydroxyapatite and Zirconia
- スイサン アパタイト ト ジルコニア ノ ショウケツ ニ ヨリ エラレタ フク
この論文をさがす
抄録
Mixtures of hydroxyapatite and zirconia containing 3mol% Y2O3 (TZ-3 Y) or 2mol% Y2O3 (TZ-2 Y) were hot-pressed under the conditions of 1300°-1400°C, 10min and 20MPa, and the bending strength and fracture toughness of the hot-pressed bodies were measured. The reactivity between hydroxyapatite and zirconia was also examined. The zirconia content was up to 50vol%. The bending strength and fracture toughness increased with an increase in zirconia content. Properties were improved with zirconia (TZ-2 Y) than with zirconia (TZ-3 Y). Compacts containing 50vol% zirconia (TZ-2 Y) fired at 1400°C showed the highest mechanical properties: bending strength; about 400MPa and fracture toughnees; about 3.0MPa·m1/2. These values were two or three times as large as those of hydroxyapatite single compacts. The following two thermal transformations were observed in the present system: (i) decomposition of hydroxyapatite to α-tricalcium phosphate and (ii) transition of tetragonal zirconia to cubic phase.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1104), 806-809, 1987
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205249072000
-
- NII論文ID
- 110002313691
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3144028
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可