- On the Formation of the 15R-type in the β-α Transformation of SiC
- ベータ-SiC ノ カネツ ニ ヨル コウゾウ ヘンカ ト 15R ノ キョドウ
この論文をさがす
抄録
The transformation of β-SiC in a high purity to α-SiC has been studied experimentally in the temperature range from 2100°C to 2300°C. The results obtained are summarized as follows:<br>1) At the initial stage of the transformation only the 6H-type was found as a newly grown phase. The 15R-type appeared always after the formation of 6H. However, the 15R thus derived disappeared with the progress of the subsequent heating. The 4H-type was not recognized throughout the present experiments.<br>2) The 6H-type has, in the range of 2100°-2300°C, a thermal stability higher than the other basic polytypes of SiC such as 3C, 4H and 15R.<br>3) The β-α transformation is considered to take place mainly through a vapour phase, because the activation energy associated with this change was estimated to be as high as 134±4kcal/mole. However, it should also be pointed out that a premonitory twinning is required to complete this transition unobstrusively.<br>4) The 15R-type is considered to grow, not direct from β-SiC, but through the 6H type already formed.<br>5) The possibility is conceived that 15R is a metastable form in the whole range of temperature. On the other hand, if a proper stable range exists for this polytype, it will be very narrow indeed, probably at about 2000°C.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 77 (889), 313-318, 1969
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680224538240
-
- NII論文ID
- 110002314975
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 8468282
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可