- Solid State Reaction between Nb<sub>2</sub>O<sub>5</sub> and CaO
- Nb2O5 CaOケイ ノ コソウ ハンノウ
この論文をさがす
抄録
Solid state reactions between sintered Nb2O5 and CaO have been studied in Ar at the temperature range from 1150°C; to 1300°C. The reaction layers formed at the Nb2O5-CaO interface were examined by using electron microscopy, EPMA, X-ray diffraction and dilatometry. The following results were obtained.<br>At 1150°C and 1200°C, three layers (CaO⋅Nb2O5, 2CaO⋅Nb2O5 and a phase mixture of cubic 3CaO⋅Nb2O5 and orthorhombic compound) and at 1250°C and 1300°C, four layers (CaO⋅Nb2O5, 2CaO⋅Nb2O5 cubic 3CaO⋅Nb2O5 and a phase mixture of cubic 3CaO⋅Nb2O5 and orthorhombic compound) were formed. These results indicated that the one-way diffusion of CaO into Nb2O5 occurred. The order in width of the reaction layer was the phase mixture, cubic 3CaO⋅Nb2O5, 2CaO⋅Nb2O5 and CaO⋅Nb2O5. The orthorhombic compound was richer in CaO content than 4CaO⋅Nb2O5. No compound richer in CaO content than orthorhombic compound was found in the temperature range 1150°C to 1300°C.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 89 (1025), 9-13, 1981
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282680225615488
-
- NII論文ID
- 110002316354
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- HANDLE
- 10191/7489
-
- NDL書誌ID
- 2302305
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可