- Corrosion of Fused Silica Refractories by Molten CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> Slag
- ヨウユウ セキエイシツ タイカブツ ノ CaO Al2O3 SiO2ケイ スラ
この論文をさがす
抄録
The corrosion of fused silica refractories in molten CaO-Al2O3-SiO2 slag was studied. The experiment was carried out with a rotating cylindrical specimen. The retults are as follows:<br>(1) The diameter of specimens decreased linearly with time. The increase both in temperature and rotating speed promoted the corrosion.<br>(2) A thin reaction layer was observed on the surface of the specimen. The change in SiO2 concentration in the slag was best described by a rate equation (which was derived) for the mass transport controlled mechanism. The apparent activation energy of corrosion was 64kcal/mol, implying that the corrosion is controlled by diffusion of ion in the slag.<br>(3) A non-dimensional equation κ=αU0.67 was obtained, the exponent of which agreed with the literature values.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 94 (1095), 1183-1185, 1986
公益社団法人 日本セラミックス協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205248595712
-
- NII論文ID
- 110002316795
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3106722
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可