多孔質セラミックスの破壊靭性評価

DOI 機関リポジトリ HANDLE Web Site Web Site 被引用文献1件 参考文献9件 オープンアクセス

書誌事項

タイトル別名
  • Evaluation of Fracture Toughness of Porous Ceramics.
  • タコウシツ セラミックス ノ ハカイジンセイ ヒョウカ

この論文をさがす

抄録

The indentation fracture (IF) method, the single-edge precracked beam (SEPB) method, and the single-edge V-notched beam (SEVNB) method were applied to evaluate the fracture toughness of four kind of porous ceramics of SiC, Al2O3 and Mg2Al4Si5O18 with porosity ranging from 37 to 43%. The microstructures of these materials were composed of ceramics grains, glassy grain boundaries and pores. Each grain was joined together with the glassy grain boundary phase. The IF and SEPB methods were not applicable because both precracks and indenter traces were not visible. On the other hand, the SEVNB method was applicable because the V-notch could be easily machined by grinding. In the case of the SEVNB method, the applied load versus back-face strain plots under four point bending showed nonlinearity prior to the maximum load. The R-curve behavior was estimated from the compliance change of specimens. The fracture toughness of porous ceramics was smaller than that of dense ceramics, and increased with increasing crack extension. Since the stable crack predominantly propagated along glassy grain boundaries, the R-curve behavior depended on the loading rate and matrix grain size. The increment of R-curve by grain briding got bigger for coarser-grain sized ceramics.

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ