リサイクル・ＰＡ６６材のＴｇ以上の環境下での高温疲労き裂進展特性に及ぼす負荷速度の影響

DOI Web Site Web Site 参考文献23件

書誌事項

タイトル別名
  • Influence of Loading Rate on Fatigue Crack Propagation Property of Recycled PA 66 Material at High-Temperature above Tg.
  • リサイクル PA66ザイ ノ Tg イジョウ ノ カンキョウ カ デ ノ コウオン ヒロウ キレツ シンテン トクセイ ニ オヨボス フカ ソクド ノ エイキョウ

この論文をさがす

抄録

In this study, high temperature fatigue crack propagation test of the engineering plastic material was carried out in order to clarify the effect of loading rate on the fatigue crack propagation property at the high temperature environment above Tg. Then, failure mechanism and loading rate dependence were evaluated. (1) The resistance against the crack propagation at 30 Hz that was high loading rate was more excellent than that at 10 Hz and 3 Hz which was low-loading rate. And, the resistance against the crack propagation at 10 Hz was equivalent to that at 3 Hz. (2) The resistance against the crack propagation of R 1 material remarkably decreased in comparison with that of virgin material. However, the resistance against the crack propagation of R 3 material was almost equal to that of R 1 material. (3) From the fractography using SEM the fracture surface at high loading rate was a brritle form, and the effect by the fatigue was big. In the meantime, that at low loading rate was a ductile form, and it seemed to overlap fatigue and creep. The viscoelastic effect of the matrix seems to remarkably appear in the fracture surface at low loading rate. (4) It was proven that the process zone dimension and the reinforced fiber length influenced the difference between fatigue crack proagation mechanism at the high loading rate and that at the low loading rate.

収録刊行物

参考文献 (23)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ