- A Study of Coefficient of Friction of UHMWPE in Various Contact Conditions and Measurement of Contact Temperature.
- チョウコウブンシリョウ ポリエチレン ノ セッショク ジョウタイ ニ ヨル マサツ ケイスウ ノ ヘンカ ト マサツメン オンド ノ ソクテイ
この論文をさがす
抄録
Wear debris of ultra high molecular weight polyethylene abbreviated as UHMWPE were clarified to be a major cause of osteolysis. So the wear rate evaluation of UHMWPE has to be performed in the research of artificial joint using UHMWPE. But wear evaluation of UHMWPE requires scrupulous procedure. As the wear rate of UHMWPE is strongly correlated to the coefficient of friction, this study was designed to assess a change of the coefficient of friction for various contact conditions. It was found that the contact condition strongly affected the coefficient of friction. Furthermore contact temperature was measured by means of the infrared radiometric microscope and was compared to the lubricant temperature. Temperature rise up to about 12°C was observed in 30 minutes under a condition of the mean contact pressure p = 12.7 MPa and sliding speed 50 mm/s. There was a linear relation between contact temperature and lubricant temperature.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 69 (677), 121-127, 2003
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679423265024
-
- NII論文ID
- 110002370282
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 6447244
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可