- Gigacycle Fatigue Behavior and Fracture Morphology of High Speed Tool Steel, JIS SKH 51.
- コウソクド コウグ コウ SKH 51 ノ チョウチョウジュミョウ ヒロウ キョドウ ト ハカイ ケイタイ
この論文をさがす
抄録
Gigacycle fatigue characteristics of high speed tool steel, JIS SKH 51, was investigated under cantilever-type rotary bending fatigue tests in an open environment at room temperature. As a result of fatigue tests, S-N curve was clearly classified into two types of fracture modes by the different crack origins. One fracture mode occurred at the surface inclusion in the region of short fatigue life and high stress amplitude level. The other was at the subsurface inclusion in the region of long fatigue life and low stress amplitude level. The transition of crack initiation site from surface to subsurface appeared at about 2×104 cycles and the stress amplitude for the transition was affected by the tempering temperature of the specimen. On the other hand, difference on fatigue life for internal fracture mode between specimens treated by different tempering temperature did not observed. Fatigue fracture mechanisms were discussed through the detailed observation of subsurface crack initiation site.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 69 (679), 662-670, 2003
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204446424448
-
- NII論文ID
- 110002370357
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD3sXjvVSns70%3D
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- HANDLE
- 10110/1682
-
- NDL書誌ID
- 6516189
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可