ポリエチレン製造用超高圧圧力容器のＬＢＢ条件の検討　Ｉ　　材料特性と内圧疲労試験結果

• 岩館 忠雄

• 竹俣 裕行

• 小林 実

• 田中 英彦

書誌事項

タイトル別名

• Study on LBB criterion of high pressure reactors for polyethylene production. 1st report Material behavior and results of internal pressure fatigue test.
• ポリエチレン セイゾウヨウ チョウコウアツ アツリョク ヨウキ ノ LBB ジ

抄録

Fracture toughness and fatigue crack growth rate behavior were investigated using six materiels with different toughness which were taken out of a tubular type reactor and heat treated at different tempering temperatures. Repeated internal pressure tests were conducted using actual size cylinders where the fracture toughness of materials ranged from 67 to 144 MPa √(m). Test results suggest that actual reactors satisfy the leak before break (LBB) condition because of their higher fracture toughness.

収録刊行物

• 日本機械学会論文集Ａ編

  日本機械学会論文集Ａ編 53 (486), 236-240, 1987

  一般社団法人 日本機械学会

キーワード

• Leak Before Break
• High Pressure Reactor
• Internal Pressure Fatigue Test
• Brittle Fracture
• Fracture Toughness
• Fatigue Crack Growth Rate

詳細情報

• CRID: 1390282679454040448
• NII論文ID: 110002377173
• NII書誌ID: AN0018742X
• DOI: 10.1299/kikaia.53.236
• ISSN: 18848338
• ISSN: 03875008
• NDL書誌ID: 3113433
• Web Site: https://ndlsearch.ndl.go.jp/books/R000000004-I3113433
• Web Site: http://www.jstage.jst.go.jp/article/kikaia1979/53/486/53_486_236/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • NDL
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可