- Fundamental study of microstructure-oriented strength assessment of a spheroidal graphite cast iron. 2nd Report. Corrosion fatigue in 3% hydrochloric acid and synthetic seawater.
- キュウジョウ コクエン チュウテツ ノ キョウド ヒョウカ ニ カンスル キソ
この論文をさがす
抄録
Ferrite-base and pearlite-base spheroidal graphite cast irons were prepared to examine corrosion fatigue resistance in 3% hydrochloric acid and synthetic seawater. Rotating bending corrosion fatigue tests were conducted at two rates 3400 rpm and 260 rpm. From the tests in air and two corrosive environments, the following results were obtained : (1) The pearlite-base material (F) showed a fatigue strength stronger than that of the ferrite-base material (A) in the intermediate-cycle fatigue range, irrespective of environment or rotating speed. In the high-cycle fatigue range, the fatigue strengths of both materials asymptotically approached to coincide. (2) Anodic dissolution of graphite and local cathodic dissolution of cementite in pearlite played a primary role in the high-cycle corrosion fatigue process. (3) Those dissolutions described above induced a fatigue process different from that in air and resulted in diminished scatter of the S-n curves.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 54 (501), 934-940, 1988
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679456367232
-
- NII論文ID
- 110002377610
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3184181
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可