• 214 Evaluation of Burst Strength of FW-FRP Composite Vessel after Impact

抄録

Impact tests of filament-wound carbon fiber composite pipes were carried out using drop-weight impact testing device developed by the authors. Depth of fiber breakage region caused by impact test was evaluated after burst strength test. Burst pressure of composite pipes was also measured in order to investigate the burst strength degradation of pressure vessels due to impact damages. It is clarified that the amount of impact damage of filament-wound composite pipes depends on the impact absorption energy. Furthermore, it is demonstrated that the burst strength of FW-FRP composite pipes after impact was decreased as the increase in cross sectional ratio of damage area.

収録刊行物

• 機械材料・材料加工技術講演会講演論文集

  機械材料・材料加工技術講演会講演論文集 2000.8 (0), 75-76, 2000

  一般社団法人 日本機械学会

キーワード

• FW-FRP composite vessel
• burst strength after impact
• drop-weight impact test

詳細情報

• CRID: 1390001205877642624
• NII論文ID: 110002485196
• DOI: 10.1299/jsmemp.2000.8.75
• ISSN: 2424287X
• Web Site: https://www.jstage.jst.go.jp/article/jsmemp/2000.8/0/2000.8_75/_pdf
• 本文言語コード: ja
• データソース種別:
  • JaLC
  • Crossref
  • CiNii Articles
• 抄録ライセンスフラグ: 使用不可