- 228 Study on Stress Corrosion Cracking of GFRP using Single Fiber Model Specimen : Evaluation of Diffusion Phenomenon into Resin
抄録
Single fiber fragmentation test have been conducted to examine the degradation of inner fiber strength surrounded by the resin using E-glass/Vinylestr model composite. Stressed and unstressed specimens under the environmental attack by water and acid have been prepared. The effect of diffusion phenomenon into the resin on inner fiber strength is investigated as a function of immersion time. As a result, the strength of fiber in stressed resin was lower than that in unstressed resin. This result indicates that stressed polymer have the diffusion phenomenon accelerated. In reference to each environment conditions (water and acid), the fiber degradation behavior was unchanged. It seemed that the water would only diffuse into the resin, and the acid would not. These experimental results were explained analytically based on Fickian diffusion analysis. It is expected that water diffusion affect the mechanism of the fiber degradation in the earlier stage than acid diffusion.
収録刊行物
-
- 機械材料・材料加工技術講演会講演論文集
-
機械材料・材料加工技術講演会講演論文集 2000.8 (0), 231-232, 2000
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205876717184
-
- NII論文ID
- 110002485368
-
- ISSN
- 2424287X
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可