144 衝撃荷重下におけるCFRP積層材の混合モード層間破壊特性(OS5-2 異物衝突損傷)(OS5 材料の衝撃強度・損傷に関する最近の知見)  [in Japanese] 144 Mixed Mode Interlaminar Fracture Behavior of Carbon-Fiber/Epoxy Composite Laminates under Impact Loading  [in Japanese]

The mixed mode (I+II) fracture behavior of carbon-fiber/epoxy composite laminates was investigated over a wide range of loading rate to clarify the effects of strain rate and mode mixture on fracture behavior. MMF (Mixed Mode Flexure) and MMB (Mixed Mode Bending) specimens were used to evaluate the mixed mode fracture toughness. The mixed mode fracture toughness clearly showed strain rate dependence regardless of mode ratio; the mixed mode impact fracture toughness was about 10 % lower than the local maximum value under static loading. Local maximum values existed at static loading rate for mixed mode fracture toughness, G_C. The mixed mode fracture toughness conform to the linear criterion for the region of high mode ratio, G_<II>/G_I=13, regardless of loading rates. However, it did not conform to the linear criterion for the region of low mode ratio, G_<II>/G_I≤3, and high loading rate, G≥10^2 J/m^2/s.