1124 AIP 法により CrN 薄膜を被覆することによるアルミニウム合金の耐摩耗性向上に関する研究  [in Japanese] Study on improvement of wear resistance of Al alloy by coating of CrN film using AIP method  [in Japanese]

By changing the quality of thin film and coating the CrN thin film which fracture does not occur when load of the high load is carried out with coating different bias voltage in wear test considered the wear resistance improvement in aluminum alloy (A2024). And the influence of coating of the multilayered film by changing the bias voltage exerted on wear resistance was considered. CrN thin film was coated on the surface of substrate was by Arc Ion Plating (AIP) method using Cr cathode and N_2 gas. In the wear test that carried out load of the high load (10N), fracture did not occur the thin film and multilayered film that were coated with low bias voltage.