超音波励起フェライトメッキ法によるNiZnフェライト膜の作製
書誌事項
- タイトル別名
-
- Preparation of NiZn Ferrite Films by Ultrasound-Enhanced Ferrite Plating
- チョウオンパ レイキ フェライト メッキホウ ニヨル NiZn フェライト マ
この論文をさがす
抄録
Polycrystalline films of spinel Fe3-x-yNixZnyO4 (x = 0−0.39, y = 0-0.3) were ferrite-plated from an aqueous solution (T = 75°C, pH = 6.8) of FeCl2 + NiCl2 + ZnCl2 to which an oxidizing solution of NaNO2 had been added. Low frequency (19.5 kHz, 600 W) ultrasound waves and high-frequency (1.6 MHz, 20 W) ultrasound waves were applied during plating. When the aqueous solutions were supplied intermittently, Fe3O4 (x = y = 0) films with a smooth surface were obtained only when low- and high-frequency ultrasound waves were applied simultaneously. On the other hand, supplying the aqueous solutions continuously facilitated formation of Fe3O4 films with a smooth surface during low-frequency sonication. The simultaneous sonication increased the solubility limit of Ni ions in Fe3-x-yNixZnyO4 films to x = 0.42 from the previous limit of x = 0.35 without sonication, though at a low deposition rate (4 nm/min).
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 22 (4_2), 473-476, 1998
公益社団法人 日本磁気学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680069512832
-
- NII論文ID
- 110002811461
-
- NII書誌ID
- AN0031390X
-
- ISSN
- 18804004
- 02850192
-
- NDL書誌ID
- 4458071
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可