Relationship Between the Degree of Conversion and Internal Discoloration of Light-activated Composite
-
- IMAZATO Satoshi
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
-
- TARUMI Hisashi
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
-
- KOBAYASHI Kyoko
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
-
- HIRAGURI Hideki
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
-
- ODA Kozo
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
-
- TSUCHITANI Yasuhiko
- Department of Operative Dentistry, Osaka University Faculty of Dentistry
Bibliographic Information
- Other Title
-
- 光重合型コンポジットレジンの重合率と変色の関係について
Search this article
Abstract
In order to elucidate the relationship between the degree of conversion and internal discoloration of light-activated composite, four experimental composites which contained different amounts of Bis-GMA and TEGDMA were prepared, and the degree of conversion and discoloration of each composite, with or without annealing, were determined. The degree of conversion was measured by Fourier transformation infrared spectroscopy and the color change was determined after 1, 2, 3 and 4 weeks of immersion in water at 60°C. The non-annealed composites demonstrated a greater degree of conversion and less discoloration as the amount of TEGDMA was increased. Annealed composites showed a significantly greater degree of conversion and less discoloration compared with the non-annealed composites. The results indicate that the greater the degree of conversion, the less the discoloration of composite, and the correlation between the two factors was significant for light-activated composite.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 14 (1), 23-30,101, 1995
The Japanese Society for Dental Materials and Devices
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679691951104
-
- NII Article ID
- 110002984162
-
- NII Book ID
- AA10443149
-
- ISSN
- 18811361
- 02874547
- http://id.crossref.org/issn/02874547
-
- PubMed
- 8940542
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed