- Tensile Fatigue Strength of Light Cure Composite Resins for Posterior Teeth
この論文をさがす
抄録
The fatigue property of the composite resin has recently been a subject of research. In this study, the fatigue strength and the tensile strength of composite resins stored in water were investigated. Two types of light cure composite resins were used: a Hybrid type and an MFR type. Dumbbell-shaped specimens were prepared. After storage at 37±0.5°C for 24 hours, 1 month, 3 months, 6 months and 12 months, the fatigue test and the direct tensile test were performed. The staircase method was employed to analyze the fatigue strength under a 105 cyclic load. The fatigue strength of the Hybrid type at 24h ours was 54.7MPa; that of the MFR type was 28.1MPa. Both fatigue strengths decreased during water storage. Otherwise, the tensile strength of the Hybrid type was 77.0MPa; that of the MFR type was 53.5MPa. After 12 months of storage, the tensile strength of the Hybrid type remained unchanged during water storage; however, that of the MFR type decreased.
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 14 (2), 175-184,277, 1995
一般社団法人 日本歯科理工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679694282496
-
- NII論文ID
- 110002984180
-
- NII書誌ID
- AA10443149
-
- ISSN
- 18811361
- 02874547
- http://id.crossref.org/issn/02874547
-
- PubMed
- 8940556
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可