Improvement of the Bonding Technique with 4-META/MMA-TBB Resin to EDTA Treated Tooth Substrates

DOI
  • SHIMIZU Hitomi
    Division of Functional Polymers, Institute for Medical and Dental Engineering, Tokyo Medical and Dental University
  • NAKABAYASHI Nobuo
    Division of Functional Polymers, Institute for Medical and Dental Engineering, Tokyo Medical and Dental University

Bibliographic Information

Other Title
  • EDTA前処理をした歯質への4-META/MMA-TBB系レジンの接着改良法

Search this article

Abstract

In our on going study of adhesion to bovine tooth substrates with 4-META/MMA-TBB resin, two painting techniques were examined to find an optimal treatment prior to bonding to EDTA pretreated tooth surface.One was the currently used single-painting technique, in which liquid monomers of the resin are applied once to pretreated tooth surface prior to bonding with the resin paste.The second was triple-painting technique, in which liquid monomers of the resin were applied to pretreated tooth surface three times prior to bonding with the resin paste.After each succeeding liquid monomers application, the prepared tooth surface becomes drier.A 1-min pretreatment with 0.3M EDTA・2Na-0.2M EDTA・Fe・Na(pH7.4)was found to be relatively effective in removing the smeared layer.Good tensile bond strengths enamel 13MPa and dentin 12MPa were obtained when the triple-painting technique was applied.A thin 1μm layer thought to be a hybrid of resin and dentin, was detected using SEM.XMA also exibited the demineralized dentin with a 1μm layer.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top