Dielectric and Piezoelectric Properties of 0.91Pb(Zn<SUB>1⁄3</SUB>Nb<SUB>2⁄3</SUB>)O<SUB>3</SUB>–0.09PbTiO<SUB>3</SUB> Single Crystals
-
- Kuwata Jun
- Department of Physical Electronics, Tokyo Institute of Technology
-
- Uchino Kenji
- Department of Physical Electronics, Tokyo Institute of Technology
-
- Nomura Shoichiro
- Department of Physical Electronics, Tokyo Institute of Technology
この論文をさがす
抄録
The dielectric, piezoelectric and elastic properties of 0.91Pb(Zn1⁄3Nb2⁄3)O3–0.09PbTiO3 single crystals have been investigated as functions of temperature and applied electric field. Two multiple phase transitions at 68°C and 178°C, the crystal changing from the rhombohedral ferroelectric phase to tetragonal ferroelectric and then to cubic paraelectric, have been observed. Both the transitions are of first-order, but both are slightly diffused. Significant increases in the dielectric, piezoelectric and elastic constants are observed at the lower transition point. In particular, the sample poled along the pseudo-cubic [001] axis reveals anomalously large piezoelectric and electromechanical coupling constants at room temperature in the rhombohedral phase (d[001]⁄⁄=1500×10−12 C/N, k[001]⁄⁄=0.92).
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 21 (9), 1298-1302, 1982
社団法人応用物理学会