Ba(Mg<SUB>1⁄3</SUB>Ta<SUB>2⁄3</SUB>)O<SUB>3</SUB> Ceramics with Temperature-Stable High Dielectric Constant and Low Microwave Loss
-
- Nomura Shoichiro
- Department of Physical Electronics, Tokyo Institute of Technology
-
- Toyama Keiichiro
- Department of Physical Electronics, Tokyo Institute of Technology
-
- Kaneta Kumiko
- Department of Physical Electronics, Tokyo Institute of Technology
この論文をさがす
抄録
A dense ceramic with an ordered perovskite structure with chemical formula Ba(Mg1⁄3Ta2⁄3)O3 is prepared, aiming at materials for a dielectric resonator with temperature-stable high dielectric contsant and low loss at microwave frequency. A small amount of Mn ion is doped to the sample to complete the sintering. The dielectric constant and unloaded Q are 25 and 16800 at 10.5 GHz respectively. The temperature coefficient of resonant frequency is estimated as 2.7 ppm/°C in the vicinity of room temperature. The value of Q we obtained is the highest among those reported so far on ceramics having a similar characteristic.
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 21 (10), L624-L626, 1982
社団法人応用物理学会