Effects of Cation Substitution on the Structural and Superconducting Properties of YBa_2Cu_3O_7 : I. Oxides :

• Yasuhiko,Syono

  Institute for Materials Research, Tohoku University

• Ayako,Tokiwa

  Institute for Materials Research, Tohoku University

• Masae,Kikuchi

  Institute for Materials Research, Tohoku University

• Keiji,Kusaba

  Institute for Materials Research, Tohoku University

• Reiko,Suzuki

  College of General Education, Tohoku University

• Tsuyoshi,Kajitani

  Institute for Materials Research, Tohoku University

• Daisuke,Shindo

  Institute for Materials Research, Tohoku University

• Norio,Kobayashi

  Institute for Materials Research, Tohoku University

• Osamu,Nakatsu

  Institute for Materials Research, Tohoku University

• Yoshio,Muto

  Institute for Materials Research, Tohoku University

抄録

90K級超伝導体の斜方晶Yba_2Cu_3O_7における陽イオン置換効果の結晶構造および超伝導特性に及ぼす影響を,X線および中性子回折,熱および化学分析,電気抵抗測定などにより調べた。Y^<3+>をより大きなイオンのLa^<3+>で置換した結果,斜方晶歪の減少とT_cの顯著な低下が見られるが,370℃,酸素中の熱処理によりT_cはかなり改善される。Ba^<2+>をLa^<3+>で,Y^<3+>をCa^<2+>で置換することにより酸素量はそれぞれ微増および微減し,いずれの場合もCuの平均原子価が減少する結果,T_cは低下した。CuをFe,Co,Ni,Znで置換した結果,3価以上の原子価をとると考えられるFe,Coで酸素量の増大と正方晶への転移,2価のNi,Znでは酸素量の減少が見られた。中性子回折の結果,CoはCu1サイト,NiはCu2サイトへの席選択捜のあることを認めた。T_cの低下はYおよびBaサイトの陽イオン置換の場合より著しく,伝導径路への不純物添加効果と見られる。

収録刊行物

• JJAP series

  JJAP series 1 42-45, 1988-05-10

  Japanese Journal of Applied Physics

詳細情報

• CRID: 1540572720307542528
• NII論文ID: 110003958821
• NII書誌ID: AA11020413
• Web Site: http://dl.ndl.go.jp/info:ndljp/pid/10472073
• 本文言語コード: en
• データソース種別:
  • NDL-Digital
  • CiNii Articles