Surface Structure on Ar<sup>+</sup>-Ion Irradiated Graphite by Scanning Probe Microscopy
-
- An Bai
- \Chugoku National Industrial Research Institute, AIST, MITI, Kure, Hiroshima 737-0197, Japan
-
- Fukuyama Seiji
- \Chugoku National Industrial Research Institute, AIST, MITI, Kure, Hiroshima 737-0197, Japan
-
- Yokogawa Kiyoshi
- \Chugoku National Industrial Research Institute, AIST, MITI, Kure, Hiroshima 737-0197, Japan
-
- Yoshimura Masamichi
- Toyota Technological Institute, Hisakata, Tempaku, Nagoya 468-8511, Japan
書誌事項
- タイトル別名
-
- Surface Structure on Ar+-Ion Irradiated Graphite by Scanning Probe Microscopy.
この論文をさがす
抄録
The surface structure of a highly oriented pyrolytic graphite (HOPG), irradiated by Ar+ ions with an ion energy of 0.5–1.0 keV at doses below 5× 1011 ions/cm2 during annealing, was characterized by scanning probe microscopy. The ion-induced hillocks were observed by both scanning tunneling microscopy (STM) and atomic force microscopy (AFM) after the ion irradiation, the heights of which, measured by STM, were larger than that measured by AFM in the tapping mode. The hillocks were recovered distinguishably by annealing above 470 K. Almost 85% of the hillocks disappeared after annealing at 1270 K and they disappeared completely after annealing above 1770 K. The behavior of defects produced by ion-irradiation in HOPG during annealing is discussed.
収録刊行物
-
- Japanese Journal of Applied Physics
-
Japanese Journal of Applied Physics 39 (6B), 3732-3735, 2000
The Japan Society of Applied Physics
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681230058496
-
- NII論文ID
- 210000047404
- 110004068925
-
- NII書誌ID
- AA10457675
-
- COI
- 1:CAS:528:DC%2BD3cXkvVynur0%3D
-
- ISSN
- 13474065
- 00214922
-
- NDL書誌ID
- 5434963
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可