Investigation of Interfacial Stresses in CF-Epoxy Composites by In-Situ Experiments and Micromechanical FE Analysis
-
- Hojo Masaki
- Department of Mechanical Engineering, Graduate School of Engineering, Kyoto University
-
- Adaji Taiji
- 京大
-
- Tanaka Mototsugu
- Department of Mechanical Engineering, Graduate School of Engineering, Kyoto University
-
- Fiedler Bodo
- ハンブルグ工大
抄録
A combined experimental and numerical study has been carried out in order to study the mechanism of initial failure in transversely loaded CF/epoxy composites. The failure initiation under transverse tensile loading was investigated in a scanning electron microscope (SEM). It was observed that interfacial failure was the dominating failure mechanism for both materials. The applied load that caused initial failure in the experiment was applied as a global load in a microscopic finite element (FE) calculation. The numerical calculation could explain the experimentally observed results. Furthermore an upper limit of the interfacial normal (INS) and shear (ISS) strength was determined.
収録刊行物
-
- 計算力学講演会講演論文集
-
計算力学講演会講演論文集 2004.17 (0), 119-120, 2004
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282680831571840
-
- NII論文ID
- 110004070250
-
- ISSN
- 24242799
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可