High Permeability Properties of Amorphous Co-Fe Base Alloys

IR

Search this article

Abstract

Amorphous alloys of (Fe_<1-x>Co_x)_<80>P_<13>C_7 and (Fe_<1-x>Co_x)_<75>Si_<15>B_<10> were prepared by rapid quenching from the melt by using two solidification techniques of centrifugal and roller types. Specimens were ribbons in form. Measurements were made of B-H hysteresis loop, effective permeability at high frequencies, longitudinal magnetostriction, electrical resistance, Vickers hardness and tensile strength. The magnetostriction is zero at a composition near x=0.94, being positive in the range of 0<x<0.94 and negative in the range of 1>x>0.94. The alloy of Fe_<4.7>Co_<70.3>Si_<15>B_<10> having a nearly zero magnetostriction exhibits the best soft magnetic properties ; the coercive force is 0.006 Oe and the maximum permeability is about 820×10^3 after annealing at 150℃ in a magnetic field. In addition, this alloy has a high effective permeability at higher frequencies up to about 100 kHz, high hardness and high tensile strength.

Journal

Details 詳細情報について

Report a problem

Back to top