An Investigation on Thermal Recycling of Recycled Plastic Resin : Combustion Characteristics of Polyethylene Terephthalate Resin Powder in a High Temperature Oxidizing Atmosphere(<Special Issue>Experimental Mechanics in Heat and Fluid Flow)

Thermal recycling of recycled plastic resin is focused in this investigation. Fine grinding of plastic resin and preparation of high temperature oxidizing atmosphere are indispensable for effective and successful burn-up of plastic resin. Polyethylene terephthalate resin powder is employed and high temperature oxidizing atmosphere is generated downstream an annular burner. Through a circular nozzle set coaxially in the closed bottom end of the annular burner, PET-powder and propane-air mixture are issued vertically upward into the high temperature oxidizing atmosphere. Temperature and O_2 concentration fields downstream the annular burner are first examined by varying the circular jet equivalence ratio with the air flow rate kept constant and without PET-powder supply. PET-powder having a mass-median diameter of either 89.7μm or 145μm is then issued into the high temperature region along with propane-air mixture by varying the PET-powder mass flow rate. Appearances of the PET-powder flame are observed using a high-speed CCD video camera and unburnt PET particles are traced during their passages in the high temperature region. Variation of O_2 concentration fields due to PET-powder combustion is also measured in the PET flame. According to the results, overall limit conditions for effective burn-up of PET-powder are finally discussed.