- Effect of Si Contents on Hardness and Conductivity by Aging of Al-0.5mass%Zr-Si Alloys Cast in Iron Mold
- テッセイ カナガタ ニ チュウゾウ シタ Al 0 5massパーセントZr ゴウキン ノ ジコウ ニ ヨル コウド ト ドウデンリツ ニ オヨボス Si テンカ ノ エイキョウ
この論文をさがす
抄録
Aluminum casting alloy with high strength, high conductivity, and heat resistance is required as the secondary conducting material for the high speed induction motor. The liquidus of Al-0.5%Zr-xSi (x=0.02-1.0 mass%) alloy were calculated by CALPHAD method, and casting temperature was decided. Effects of Si content on hardness and conductivity changes during aging at 623-723 K of Al-0.5 mass%Zr-xSi alloys cast process in iron mold were studied, and the heat resistance at 423 K for alloy with optimum characteristic was investigated. A small addition of Si accelerated the hardening and high conductivity of the Al-0.5 mass%Zr remarkably. The maximum hardness was obtained by aging at 673 K. Hardness and conductivity of Al-0.5%Zr-0.45%Si alloy aged at 673 K for 28.8 ks was 61.7 HB and 55 IACS%, respectively, and these characteristics in room temperature hardly changed by isothermal treatment at 423 K.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 71 (711), 1580-1586, 2005
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204478679680
-
- NII論文ID
- 110004999121
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD28XhtlGqtr4%3D
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 7741813
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可