- 10114 Characterization of Thermal Shock Fracture Behavior of SiC Whisker-Reinforced Alumina-Zirconia Ceramics
抄録
Thermal shock fracture behavior in SiC whisker reinforced alumina/zirconia ceramics was evaluated by Disc-on-Rod test in which the central region of heated specimen was quenched by means of contacting with a cool copper rod. The specimen was sintered by a hot press and a precrack was introduced. AE signals during crack growth behavior were detected by AE sensor which was attached on the rod. And using the virtual crack closure method, thermal stress and stress intensity factor were calculated from the temperature distribution measured by IR camera. The fracture resistance at the onset of crack growth was equivalent to monolithic alumina ceramics. On the other hand, the crack growth resistance was much larger than alumina ceramics, then the crack was arrested in the specimen. Consequently, it was demonstrated that the multiple toughening mechanism (crack bridging and phase transformation toughening) contributed the enhancement of crack growth resistance thermal shock.
収録刊行物
-
- 日本機械学会関東支部総会講演会講演論文集
-
日本機械学会関東支部総会講演会講演論文集 2005.11 (0), 209-210, 2005
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205846119040
-
- NII論文ID
- 110006205749
-
- ISSN
- 24242691
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可