03aC16 化学溶液塗布法による(Nd_<1/3>Eu_<1/3>Gd_<1/3>)Ba_2Cu_3O_x酸化物超伝導体の結晶成長(結晶評価・その場観察(2),第36回結晶成長国内会議)
書誌事項
- タイトル別名
-
- 03aC16 Growth of (Nd_<1/3>Eu_<1/3>Gd_<1/3>)Ba_2Cu_3O_x superconductors by metal organic deposition method(NCCG-36)
この論文をさがす
抄録
The as-deposited (Nd_<1/3>Eu_<1/3>Gd_<1/3>)Ba_2Cu_3O_x (NEG123) films on MgO(100) substrates by metal organic deposition (MOD) method are amorphous and turns into crystalline when it is heated around 900℃. The growth mechanism of MOD is still not yet to understand. In this work, we report in situ observation of growth process of NEG123 films using a high temperature optical microscope. High temperature optical microscope clearly shows that (1) a larger amount of white particles appear at around 890℃, (2) NEG123 plate-like crystals with facet faces are formed in the white particles and (3) many NEG211 needle crystals are grown from flux (Ba and Cu rich particles) at a rate of about 7.5μm/sec.
収録刊行物
-
- 日本結晶成長学会誌
-
日本結晶成長学会誌 33 (4), 339-, 2006
日本結晶成長学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205898372736
-
- NII論文ID
- 110006208591
-
- NII書誌ID
- AN00188386
-
- ISSN
- 21878366
- 03856275
-
- HANDLE
- 10297/2757
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可