Compressive Strength, Surface Roughness, Fluoride Release and Recharge of Four New Fluoride-releasing Fissure Sealants

The aim of this study was to investigate the compressive strength and surface roughness of two glass ionomer cements and two resin-based fissure sealants before and after fluoride release and recharge. Twenty-one specimens were prepared and divided into three groups for each material. First group was loaded in compression until failure. Fluoride released was measured from the remaining specimens, and then the second group of seven specimens was loaded at 28^<th> day. The remaining seven specimens were exposed to 0.05% NaF solution and 1.23% APF gel. Fluoride amount was measured, and the last group was loaded at 70^<th> day. Surface roughness measurement of five more disk-shaped specimens from each material was also carried out. After exposure to APF gel, all materials were recharged. At the end of experimental period, it was found that surface roughness increased, whereas compressive strength decreased, over time. In conclusion, fluoride-releasing fissure sealants could act as show, rechargeable fluoride release systems. However, if a fissure sealant exhibited high fluoride release, it had inferior mechanical properties.