- Effect of Al Content on the Structure of Thin Oxide Films on the Hot-Dipped Zn-Al Coated Steel Sheets
- 溶融Zn-Al系めっき鋼板上酸化膜の皮膜構造に及ぼすAlの影響
- ヨウユウ Zn Alケイメッキ コウハン ジョウ サンカ マク ノ ヒマク コウゾウ ニ オヨボス Al ノ エイキョウ
この論文をさがす
抄録
Electronic structures of oxide films on hot-dipped Zn-0.2%Al, Zn-5%Al, and Zn-55%Al coated steel sheets have been investigated by means of the synchrotron radiation photoemission spectroscopy and compared with those of Zn and Al pure metal sheets. The oxide films were prepared by 85 hour exposure in air saturated with water vapor at 323K. The oxide film on Zn-0.2%Al had the same photoemission spectrum as the pure Zn metal, while Zn-5%Al and Zn-55%Al were similar to the pure Al in the form of photoemission spectrum. It was found that the electronic structure of the oxide films and the depth profile of the ratio of zinc oxide to aluminum oxide are varied with the ratio of Zn to Al in the alloys. The corrosion resistance of Zn-Al alloys is discussed being related to the electronic structure of the oxide films.
収録刊行物
-
- 材料
-
材料 55 (11), 986-990, 2006
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205418251392
-
- NII論文ID
- 110006570854
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 8576664
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可