- Impact Tensile Properties of 6061 and 7075 Aluminum Alloys Affected by Environmental Hydrogen
- カンキョウ スイソ ノ エイキョウ オ ウケタ 6061 オヨビ 7075 アルミニウム ゴウキン ノ ショウゲキ ヒッパリ トクセイ
この論文をさがす
抄録
Impact tensile properties of T6-aged 6061 and 7075 aluminum alloys affected by atmospheric hydrogen were investigated. In order to introduce hydrogen from the atmosphere, the alloys were pre-deformed by a slow strain rate testing (SSRT) in a humid air atmosphere with a relative humidity of 90%. For the pre-deformed specimens, the impact tensile tests were performed using split Hopkinson pressure bar (SHPB) method at an average strain rate of 5.0×10^2s^<-1>. Hydrogen concentration after the pre-deformation by SSRT was measured with a thermal desorption analysis. As a set of the experiments, it was shown that the ductility in the impact test decreased when the T6-aged 7075 alloys were hydrogen charged. The hydrogen embrittlement sensitivity of the T6-aged 6061 alloys was lower than that of the T6-aged 7075 alloys. The decrease of the ductility due to hydrogen charging of the T6-aged 7075 alloys was closely related to the increase in the ratio of the intergranular fracture near the specimen surface.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 75 (759), 1630-1638, 2009
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204477944192
-
- NII論文ID
- 110007482716
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- NDL書誌ID
- 10505405
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可